8 micrographs for keyword bone, ordered by micrograph number.
Micrograph
114
:
Poly (lactic-co-glycolic acid) (PLGA) porous scaffold for tissue engineering. Average Pore Size 350-550 micrometre, porosity estimated at 35-45% System: Poly (lactic-co-glycolic acid) (PLGA), Composition: Not specified Scanning electron microscopy (SEM) 3 mm |
|
Micrograph
115
:
Poly (lactic-co-glycolic acid) (PLGA) porous scaffold for tissue engineering. Average Pore Size 350-550 micrometre, porosity estimated at 35-45% System: Poly (lactic-co-glycolic acid) (PLGA), Composition: Not specified Scanning electron microscopy (SEM) 250 μm |
|
Micrograph
116
:
Poly (lactic-co-glycolic acid) (PLGA) porous scaffold for tissue engineering. Enlargement of a Pore. Average Pore Size 350-550 mm, porosity estimated at 35-45% System: Poly (lactic-co-glycolic acid) (PLGA), Composition: Not specified Scanning electron microscopy (SEM) 250 μm |
|
Micrograph
117
:
Sintered disc of Hydroxyapatite (Ca10(PO4)6(OH)2), a calcium phosphate ceramic with similar composition to natural bone mineral System: Hydroxyapatite (Ca10(PO4)6(OH)2), Composition: Not specified Scanning electron microscopy (SEM) 18 μm |
|
Micrograph
118
:
Poly (lactic-co-glycolic acid) (PLGA) porous scaffold for tissue engineering. Average Pore Size 100-300 µm, porosity estimated at 65% System: Poly (lactic-co-glycolic acid) (PLGA), Composition: Not specified Scanning electron microscopy, environmental 400 μm |
|
Micrograph
172
:
Bone china (with sensitive tint plate) System: Bone china, Composition: China clay 25, stone 30, bone 45 (wt% typical) Transmitted polarised light microscopy, with sensitive tint plate 100 μm |
|
Micrograph
173
:
Bone china, showing the glaze on the surface (with sensitive tint plate) System: Bone china, Composition: China clay 25, stone 30, bone 45 (wt% typical) Transmitted polarised light microscopy, with sensitive tint plate 250 μm |
|
Micrograph
174
:
Bone china (with sensitive tint plate) System: Bone china, Composition: China clay 25, stone 30, bone 45 (wt% typical) Transmitted polarised light microscopy, with sensitive tint plate 250 μm |