6 micrographs for system LAS: Li2O-Al2O3-SiO2, ordered by micrograph number.


Link to full record for micrograph 160 Micrograph 160 : Glass ceramic, heat treated at 750° C for 3 hours
System: LAS: Li2O-Al2O3-SiO2, Composition: Not specified
Transmitted polarised light microscopy, with sensitive tint plate
100 μm
Link to full record for micrograph 161 Micrograph 161 : Glass ceramic, heat treated at 750°C for 3 hours
System: LAS: Li2O-Al2O3-SiO2, Composition: Not specified
Transmitted polarised light microscopy
100 μm
Link to full record for micrograph 162 Micrograph 162 : Glass ceramic, heat treated at 840°C for 3 hours
System: LAS: Li2O-Al2O3-SiO2, Composition: Not specified
Transmitted polarised light microscopy, with sensitive tint plate
100 μm
Link to full record for micrograph 163 Micrograph 163 : Glass ceramic, heat treated at 840°C for 3 hours
System: LAS: Li2O-Al2O3-SiO2, Composition: Not specified
Transmitted polarised light microscopy
100 μm
Link to full record for micrograph 164 Micrograph 164 : Glass ceramic, heat treated at 900°C for 3 hours
System: LAS: Li2O-Al2O3-SiO2, Composition: Not specified
Transmitted polarised light microscopy, with sensitive tint plate
100 μm
Link to full record for micrograph 165 Micrograph 165 : Glass ceramic, heat treated at 900°C for 3 hours
System: LAS: Li2O-Al2O3-SiO2, Composition: Not specified
Transmitted polarised light microscopy
100 μm